Re: More Stratasys Questions

From: RP Solutions (rps@dircon.co.uk)
Date: Mon Oct 23 2000 - 13:42:03 EEST


Jorn,

What did you mean by your last e-mail? it is not clear what you are trying to say?

yours

Oliver Cole

Technical Director
RP Solutions

  
  ----- Original Message -----
  From: JBVentures
  To: RP Solutions ; rp-ml@bart.lpt.fi
  Sent: Monday, October 23, 2000 9:33 AM
  Subject: Re: More Stratasys Questions

  For Stratasys claiming to be world-leader in sales-units of RP Machines, the amount of response of it's users to this question is overwelming!
   
  Jorn Berends
  JB Ventures BV - the Netherlands
    
    -----Original Message-----
    From: RP Solutions <rps@dircon.co.uk>
    To: rp-ml@bart.lpt.fi <rp-ml@bart.lpt.fi>
    Date: Thursday, October 19, 2000 1:32 PM
    Subject: More Stratasys Questions

    Hi List,

    I have saved up a few questions that have been bugging me over the last few months.

    Question 1.
    Model Warping on the Stratasys FDM 8000: we have been making sand casting masters (typically 500mm cubed) recently which have sections 5-10mm thick in places, if we create solid parts they tend to warp/bend around the base area (sometimes the geometry of the parts determines the orientation).

    My guess is that the parts are warping due to a build up of heat from the build filament, to try and counteract this we have done the following:

    1.Create a honeycomb structure with Part Cross Hatch command in Quickslice 6.1( this works OK but parts have to be checked manually to ensure that they have no holes )

    2. Create a support base 20 layers thick.( this works OK when used with the above )

    3. Create "feet" in modelling material to help anchor the part more securely to the foam base. ( does'nt really work as internal stresses are sometimes great enough to pull the parts off the base )
     
    4. Put pauses on each slice to allow heat to dissipate ( I haven't tried this yet but it kinda goes against the grain to deliberately build parts more slowly! )

    Is there a better way of building these parts? or am I missing something? all assistance as usual gratefully recieved.

    Question 2.
    T10 Tips on the Stratasys FDM 2000
     I am interested to hear of other users experiences using T10 Tips, do you get a noticeable improvement in part finish? are there any problems using the T10 tips? does it extend the envelope of the small parts you can build? Anyone tried it on a 1650?

    Question 3.
    Waterworks Support structure: I was asked by a colleague if it was possible to Investment Cast parts ( burning out the ABS master) built using the waterworks support system, I think he was interested to see if the finish was good enough to cast enclosed areas without any hand finishing. Anyone tried it?How reliable is Waterworks?what about inclusions/porosity?

    Thanks in advance, all information gratefully recieved.

    Oliver Cole
    Technical Director
    RP Solutions

    Tel: 02476 632 120

    Fax: 02476 632 131

      