Andy: We can cast geometries in any air meltable ferrous or nonferrous alloy
including ductile iron by investment casting which are impossible by sand
casting.
At 09:43 PM 3/24/99 EST, you wrote:
>In a message dated 99-03-23 11:25:14 EST, you write:
>
><< >> Dan: We pour ductile iron (3-1/2 weeks) from RP patterns (1-week). >>
>As I understand, ductile iron, is done more commonly in sand casting. The
>patterns need to be either designed for that process, or converted into
>patterns that would work, as a matchplate for instance. Most sand casting
>foundries aren't geared towards prototype work though. That is the process I
>would investigate rather than investment casting.
>Andy Scott
>Lockheed Martin Aerospace
>